http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-106398207-B
Outgoing Links
Predicate | Object |
---|---|
classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/Y02E60-13 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08L79-04 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08J5-18 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01G11-48 |
filingDate | 2016-10-28-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2018-11-30-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2018-11-30-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-106398207-B |
titleOfInvention | A kind of preparation method and its super capacitor performance of polypyrrole film |
abstract | The present invention relates to a kind of polypyrrole film and its preparation method and application, the polypyrrole film is to have absorption peak at 320,440,463 and 540 nm in wavelength;The characteristic absorption of the infrared spectroscopy of the polypyrrole film is 1545 cm –1 、1466 cm –1 、1305 cm –1 、1182 cm –1 、1092 cm –1 、1043 cm –1 、915 cm –1 、787 cm –1 And 678 cm –1 .The present invention also provides the preparation methods of the polypyrrole film.The purposes of polypyrrole film is used for working electrode and supercapacitor.Large scale synthesized by the present invention, film of poly pyrrole of controlling oneself, are not only suitable for the basic materializations properties such as mechanics, electronics and the optics of research polypyrrole film;And facilitate cutting, it is suitable for assembling flexible super capacitor or battery. |