http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-106391014-B
Outgoing Links
Predicate | Object |
---|---|
classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C02F2305-10 |
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C02F1-30 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B01J35-004 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B01J23-72 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C02F1-30 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B01J23-72 |
filingDate | 2016-09-12-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2019-04-09-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2019-04-09-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-106391014-B |
titleOfInvention | Titanium dioxide/copper oxide composite oxide nano-material preparation method |
abstract | The invention belongs to functional material preparation technical fields, are related to a kind of preparation method of titanium dioxide/copper oxide composite oxide nano-material, acetylacetone copper are dissolved in DMF solution, solvent thermal reaction, obtain the DMF solution of nano cuprous oxide after cooling.Butyl titanate is dissolved in oxalic acid aqueous solution, then the DMF solution of nano cuprous oxide is added, after the condition solvent evaporated for heating and stirring, cross-linking reaction is carried out, is then heat-treated i.e. acquisition titanium dioxide/copper oxide composite oxide nano-material in Muffle furnace.Present invention process is simple and easy to do, and purity is high is uniformly dispersed, impurity content is low, and product preparation cost is low, has excellent performance.Titanium dioxide prepared by the present invention/copper oxide composite oxide nano-material uses catalytic activity with higher as catalysis material, and in degradation of dye waste water and indoor harmful gas, the fields such as photocatalysis disinfection are with a wide range of applications. |