http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-106340400-B
Outgoing Links
| Predicate | Object |
|---|---|
| classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/Y02E60-13 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/Y02E60-10 |
| classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/H01G11-86 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/H01M4-625 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/H01G11-32 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/H01M4-485 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/H01G11-46 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B82Y30-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B82Y40-00 |
| classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01M4-485 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01G11-46 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01G11-32 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B82Y40-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B82Y30-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01G11-86 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01M4-62 |
| filingDate | 2016-09-09-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| grantDate | 2018-02-23-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationDate | 2018-02-23-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationNumber | CN-106340400-B |
| titleOfInvention | A kind of carbon coating rhombic system nano bar-shape Nb2O5Material and preparation method thereof |
| abstract | The invention belongs to field of lithium ion battery, more particularly, to a kind of carbon coating rhombic system nano bar-shape Nb 2 O 5 Material and preparation method thereof, this method comprise the following steps：Oleic acid and trioctylamine are proportionally well mixed to obtained mixture A；Then a certain amount of niobic acid ammonium oxalates is added to stirring in mixture A and obtains solution B；Solution B is subjected to microwave hydrothermal reaction；The product obtained after being reacted in step 3 is centrifuged, and obtains solidliquid mixture C；Finally solidliquid mixture C is put into tube furnace and carries out calcination processing.By Nb made from above-mentioned preparation method 2 O 5 Material is used to prepare lithium-ion mixture super capacitor.Carbon coating rhombic system nano bar-shape Nb prepared by the present invention 2 O 5 Material, solves currently used Nb 2 O 5 The problem of material capacity is low, high rate performance is poor, also it is conductive can it is good, preparation method is simple and easy, cost is cheap and the advantages that suitable large-scale production. |