http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-106278254-B
Outgoing Links
| Predicate | Object |
|---|---|
| classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B2235-386 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B2235-96 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B2235-3229 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B2235-3227 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B2235-3217 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B2235-48 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B2235-447 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B2235-3409 |
| classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B35-48 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C04B35-622 |
| classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B35-622 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C04B35-48 |
| filingDate | 2016-08-09-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| grantDate | 2019-04-12-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationDate | 2019-04-12-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationNumber | CN-106278254-B |
| titleOfInvention | A high-strength and high-toughness ceramic composite material and its application in the manufacture of cutting tools |
| abstract | The invention discloses a high-strength and high-toughness ceramic composite material and its application in the manufacture of cutting tools. The ceramic composite material is prepared from the following raw materials in parts by weight: zirconia, 55-65 parts; alumina, 20-30 parts ; Cerium oxide, 6-8 parts; Lanthanum oxide, 4-6 parts; Borax, 3-5 parts; Boron nitride, 1-3 parts; Zinc dialkyldithiophosphate, 2-4 parts; Sodium alginate , 0.6-0.8 part; sodium lignosulfonate, 0.4-0.6 part; sodium hexametaphosphate, 0.8-1.2 part; polyethylene glycol, 1-3 part; deionized water, 7-9 part. The ceramic composite material provided by the invention has high hardness and wear resistance, is suitable for preparing ceramic cutting tools, and is used for cutting and cutting high-hardness materials, and is not easy to be broken by aging; the preparation process of the ceramic composite material is simple and feasible. |