http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-105833349-B
Outgoing Links
Predicate | Object |
---|---|
classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/A61L2300-30 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/A61L2300-412 |
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/A61L27-3637 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/A61L27-56 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/A61L27-54 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/A61L27-58 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/A61L27-18 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/A61L27-18 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/A61L27-36 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/A61L27-58 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/A61L27-56 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/A61L27-54 |
filingDate | 2016-04-21-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2019-04-23-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2019-04-23-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-105833349-B |
titleOfInvention | A kind of preparation method of spirulina polymer composite tissue engineering bracket |
abstract | A kind of preparation method of spirulina polymer composite tissue engineering bracket, this method is that the ratio of spirulina crude extract and polymer 1:2~20 in mass ratio is dissolved in the mixed solution that organic solvent is configured to mass concentration 10~25%, stir 24~48h, it is uniformly mixed again with the pore-foaming agent of 7~10 times of mixed solution solid masses, then it is poured after being air-dried at room temperature 24~72 hours in the mold of required shape, it is again at 0.001~0.01Mpa temperature is 50~70 DEG C in vacuum degree, dry 24~48h, the sample taken out in mold immerses in deionized water, every 4~8h replaces deionized water, sample is pulled out after amounting to replacement 18~40 times, by sample vacuum degree be 0.001~0.01MPa, temperature is at 40~70 DEG C, dry 2 4~48h to obtain the final product.The spirulina polymer composite tissue engineering bracket that this method obtains has the characteristics that good hydrophilic property, compressive strength height, fast degradation, nontoxic. |