| titleOfInvention | Sheet Ag2S loaded Ags3PO4Nanosphere composite visible light catalyst and preparation method thereof |
| abstract | The present invention relates to a kind of sheet Ag 2 S loaded Ags 3 PO 4 Nanosphere composite visible light catalyst and preparation method thereof.It is characterized in that：It is by sheet Ag 2 The S and Ag for being grown in surface 3 PO 4 Nanosphere forms.Prepare 1), using the mixed solution of ethylenediamine and water be solvent in 150 170 DEG C of hydro-thermal reactions by zinc source compound and sulphur source compound, sheet ZnS materials are prepared, it is stand-by；2) after mixing, 90 100 DEG C of reactions, post processing obtains sheet Ag to the material and silver nitrate solution that, step 1) is obtained 2 S material；3), at 15 25 DEG C by Ag 2 S material is added to AgNO 3 Aqueous solution, lucifuge stirring, then under magnetic stirring, Na is added dropwise 3 PO 4 Solution, is added dropwise rear lucifuge and continues to react, post-process to obtain the final product.This composite material is as visible light catalyst and Ag 3 PO 4 Compare, its photocatalysis performance can be significantly improved. |