| classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08G77-38 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C09K3-10 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C09J11-04 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08K3-36 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08L83-04 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C09J183-04 |
| filingDate | 2015-09-25-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| grantDate | 2018-05-08-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationDate | 2018-05-08-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationNumber | CN-105111443-B |
| titleOfInvention | High transparency one-component condensed room temperature vulcanized silicone rubber composition and preparation method |
| abstract | The invention discloses a kind of high transparency one-component condensed room temperature vulcanized silicone rubber composition and preparation method, the composition is made of following components in parts by weight：Multiple reactionness end-group termination polymethylphenylsiloxane, 100 parts；Reinforced filling, 1~50 part；Crosslinking agent, 0.1~15 part；Catalyst, 0.1~5 part；Tackifier, 0.1~5 part.Light transmittance is up to more than 90% after product produced by the present invention cures, and mechanical strength is up to more than 2.0MPa after curing, and elongation at break is up to more than 300%. |