http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-105108380-B
Outgoing Links
| Predicate | Object |
|---|---|
| classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B23K35-40 |
| classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B23K35-362 |
| classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B23K35-362 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B23K35-40 |
| filingDate | 2015-07-31-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| grantDate | 2017-12-12-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationDate | 2017-12-12-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationNumber | CN-105108380-B |
| titleOfInvention | The preparation method of flux material composition and scaling powder |
| abstract | The invention discloses the preparation method of a kind of flux material composition and scaling powder, the composition includes epoxy resin, nano calcium oxide, acetone, sodium nitrate, acrylic resin and septichen；Wherein, relative to the epoxy resin of 100 parts by weight, the content of the nano calcium oxide is 15 parts by weight, the content of the acetone is 10 30 parts by weight, the content of the sodium nitrate is 1 10 parts by weight, the content of the acrylic resin is 10 20 parts by weight, and the content of the septichen is 5 30 parts by weight.Above-mentioned design is by the way that epoxy resin, nano calcium oxide, acetone, sodium nitrate, acrylic resin and septichen are mixed with certain proportion, scaling powder is made, and by flux application made from the above method in solder, so that the solder added with above-mentioned scaling powder can have more preferable performance in actual use, solder skip rate is substantially reduced, improves welding quality. |
| priorityDate | 2015-07-31-04:00^^<http://www.w3.org/2001/XMLSchema#date> |