http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-104995215-B
Outgoing Links
Predicate | Object |
---|---|
classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08L2207-02 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08L2205-025 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08L2205-02 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08L2308-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08L2201-10 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08L2314-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08L2314-02 |
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08L19-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08L23-142 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08L23-10 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08L23-12 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08F10-06 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08F2-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08L23-14 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08L23-12 |
filingDate | 2013-12-05-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2017-05-31-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2017-05-31-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-104995215-B |
titleOfInvention | With the rigidity for improving and the clear, thin-walled packaging material of mobility |
abstract | Heterophasic polypropylene resin,It has the MFR (2.16kg determined according to ISO 1133 more than 27g/10min,230℃),It includes Noblen or polymer matrices (A) and the EP rubbers phase (B) being dispersed in described matrix,Wherein,The heterophasic polypropylene resin has the indissolvable component (XCU) in 25 DEG C of paraxylene of the amount of 75 to 85wt%,It has the weight average molecular weight measured by gpc analysis according to ISO 16,014 1 and 16,014 4 of 110 190kg/mol,The monomeric unit for coming from ethene of the amount of indissolvable component (XCU) containing 12.0wt% to 21.0wt% of the paraxylene at 25 DEG C,With the amount of 15wt% to 25wt% 25 DEG C of paraxylene soluble constituent (XCS),It has the inherent viscosity determined according to DIN EN ISO 1,628 1 and 1,628 3 of 1.4 to 2.0dl/g,And the propylene monomer units by the amount of 40wt% or more are constituted,And with the glass transition temperature Tg for passing through dsc measurement according to ISO 6,721 7 in the compression molded samples of XCS components composition in the range of 60 to 50 DEG C. |