titleOfInvention | Crosslinking with radiation polyethylene terephthalate composite and preparation method thereof |
abstract | The invention discloses a kind of crosslinking with radiation polyethylene terephthalate composite and preparation method thereof, belong to technical field of composite materials.Solving polyethylene terephthalate bulk material in prior art cannot the technical problem of crosslinking with radiation under conventional environment.The preparation method of this composite is: after first drying the polyethylene terephthalate of 100 weight portions and the polyhedral oligomeric silsesquioxane containing multiple double bond structures of 1~10 weight portion, mix, obtain mixed material, then mixed material is joined in double screw extruder, after extruding pelletization, then by pellet injection moulding, obtain products formed, then by products formed Co 60 source or electron accelerator irradiation, composite is obtained.This composite has excellent heat resistance and mechanical property, and tensile strength is 54~69MPa, and stretch modulus is 1670~3010MPa, and heat distortion temperature is 69~101 DEG C. |