titleOfInvention | A kind of production method of polyvinyl chloride hollow fiber microfiltration membranes |
abstract | The present invention relates to a kind of production method of polyvinyl chloride hollow fiber microfiltration membranes, each substances in percentage by weight meter, polyvinyl chloride 16-25%, composite pore-forming 10-30%, balance of solvent are carried out according to the following steps:(1) by polyvinyl chloride, a certain amount of solvent input agitator, dissolving in 24 hours is stirred at 80 DEG C and forms uniform solution;(2) composite pore-forming and balance solvent are put into, continues to be stirred 24 hours at 80 DEG C;(3) deaeration in 48 hours is stood after filtering, and is cooled to 55 DEG C and obtain casting solution;(4) with conventional dry-wet spinning.The polyvinyl chloride hollow fiber microfiltration membranes for preparing in the process of the present invention, tensile strength is more than 2.5MPa, and bubble point pressure is 0.03-0.4MPa, and intensity is ensure that while uniform large aperture is obtained, and can be applied to the projects such as sewage disposal, concentrating and separating. |