titleOfInvention | With the production technology of the tin bronze tempered bead wire of rubber high adhesion |
abstract | The invention discloses a kind of production technology of the tin bronze tempered bead wire with rubber high adhesion, comprise the following steps:1. steel wire, is chosen;2., temper;3., cathodic pickling;4., bronze (copper-tin alloy) electroplating;5., washing drying;6. water base primary coat liquid, is coated;7. organic coating, is coated;8., take-up.Silane coupler in the water base primary coat liquid that the technique is used, strand one end hydrolysising group is hydrolyzed, react and combine with steel wire matrix, the organic group of the other end can react with the organic principle in final treatment techniques, effectively connect inorganic metal and organic resin, Steel Wire Surface binding efficiency after bonding force and the bonding between steel bead wire and rubber is improved, and extends the steel wire holding time. |