classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08F293-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/D01F6-92 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08F220-10 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08F220-24 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/D01D5-08 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C07C227-18 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/D01F1-10 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C07C229-08 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/D06M15-21 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08G63-183 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08G63-86 |
filingDate | 2014-12-31-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2016-08-31-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2016-08-31-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-104562279-B |
titleOfInvention | A kind of low-shrinkage anti-wicking polyester industrial fiber and manufacture method thereof |
abstract | The present invention relates to a kind of low-shrinkage anti-wicking polyester industrial fiber and manufacture method thereof.Cut into slices as raw material with the thickening of modified poly ester, process through melt spinning and anti-wicking and prepare;Described modified poly ester is made up of with amino ethylene glycol fatty acid polyester, described amino ethylene glycol fatty acid is dispersed in the molecule interchain of described polyester, and the molecule interchain of described amino ethylene glycol fatty acid and described polyester has hydrogen bond action, described amino ethylene glycol fatty acid is made to fix with the relative position of the strand of described polyester;Containing perfluoroalkyl (methyl) acrylate, non-fluorinated alkylsilane (methyl) acrylate and the ternary block polymer containing uvioresistant group in anti-wicking agent.It is high that product had both had the intrinsic fracture strength of ultralow contraction terylene industry silk, the features such as dry shrinkage is little, possess again good hydrophobic performance and preferable resistance to UV aging, in fields such as high-grade lamp box advertisement cloth, waterproof cloth and swimming pool fabrics, there is application prospect widely. |