| titleOfInvention | A kind of ferronickel phosphorus/nanometer V8C7Composite plating solution |
| abstract | The invention discloses a kind of ferronickel phosphorus/nanometer V 8 C 7 Composite plating solution, the composite plating formula of liquid is as follows：70 120 g/l of nickel sulfate, 10 20 g/l of nickel chloride, 40 80 g/l of ferrous sulfate, 10 20 g/l of frerrous chloride, 20 40 g/l of sodium hypophosphite, 10 25 g/l of boric acid, 0.1 0.5 g/l of complexing agent, 0.1 0.5 g/l of brightener, 25 grams of stabilizer, nanometer V 8 C 7 5 20 g/l.Using composite plating solution of the invention compared with prior art, can prepare with ferronickel phosphorus non-crystalline alloy as matrix, nanometer V 8 C 7 It is the composite deposite of the second phase, surface is non-microcracked.With high abrasion, corrosion resisting property.Composite plating solution composition is simple, and harm of each reagent to environment is small, and process stabilizing is simple to operate, and current efficiency is high. |