http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-104388792-B
Outgoing Links
Predicate | Object |
---|---|
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C22C29-12 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C22C29-00 |
filingDate | 2014-10-31-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2016-06-08-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2016-06-08-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-104388792-B |
titleOfInvention | A kind of high temperature resistant cermet material and its preparation method |
abstract | The invention belongs to sintering metal field, the present invention discloses a kind of high temperature resistant cermet material and its preparation method, and described high temperature resistant cermet material comprises following material: nickel sesquioxide to be 11-22 part, magnesium oxide be 5-11 part, zirconium diboride to be 7-11 part, thorium dioxide be 2-4 part, bismuth oxide to be 4-7 part, zinc be 5-9 part, copper to be 7-13 part, germanium be 2-4 part, iron are 12-17 part. Preparation method's step is as follows: each metal and stupalith high-speed mixing are carried out short mix by (1); (2) the material ball mill mixing equal is carried out ball milling; (3) cermet material being carried out high-temperature laminating in hot pressing furnace after ball milling, and be raised by in-furnace temperature as 720-780 DEG C, insulation, and continue to raise hot pressing in-furnace temperature and be 1520-1610 DEG C, sintering, cooling, is prepared as high temperature resistant cermet material. |
priorityDate | 2014-10-31-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
type | http://data.epo.org/linked-data/def/patent/Publication |