http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-104261695-B
Outgoing Links
| Predicate | Object |
|---|---|
| classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C03C17-25 |
| classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C03C17-23 |
| filingDate | 2014-09-19-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| grantDate | 2016-06-22-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationDate | 2016-06-22-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationNumber | CN-104261695-B |
| titleOfInvention | A kind of preparation method of transparent hydrophobic Zinc oxide coating |
| abstract | The present invention relates to a kind of method preparing transparent hydrophobic Zinc oxide coating on the glass substrate, comprise the following steps: the pretreatment of a. substrate；B. the preparation of zinc oxide colloidal sol；C. the preparation of Zinc oxide coating；D. the surface modification of Zinc oxide coating。Compared with prior art, the beneficial outcomes of the present invention is: apparatus and process is simple, with low cost, and reaction condition is gentle, is conducive to industrial mass production。By transparent hydrophobic Zinc oxide coating prepared by this method, there is hydrophobicity and the transparency of excellence: contact angle is more than 160 °, and roll angle is less than 8 °, and water droplet freely can roll on coating, has better self-cleaning performance；Light transmittance is close to 90%, close with blank glass, has good visible light permeability。The surface modifier used in the present invention is alkyl silane coupling agent, and non-fluorochemical is with low cost, and the less pollution to environment, modified coating is more stable。 |