http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-103915633-B
Outgoing Links
Predicate | Object |
---|---|
classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/Y02E60-50 |
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/H01M4-96 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/H01M4-9083 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/H01M4-9016 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/H01M4-9041 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01M4-90 |
filingDate | 2014-04-01-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2016-08-24-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationDate | 2016-08-24-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-103915633-B |
titleOfInvention | A kind of composite carbon fiber supported metal catalyst and its preparation method and application |
abstract | The present invention relates to a kind of composite carbon fiber supported metal catalyst and its preparation method and application, transition metal oxide is used to load derivant prepare degree of graphitization height as graphitization reinforcing agent and the metal dispersion of material with carbon element, catalyst metal particles good dispersion, the composite carbon fiber supported metal catalyst that catalytic performance is excellent.Present invention preparation is loaded with the composite carbon fibrous material of transition metal oxide, under hot conditions, transition metal oxide is catalyzed, and obtains the material with carbon element of more high graphitization degree, and using this transition metal oxide composite carbon fibrous material as catalyst carrier, reduce through reducing agent.The initial electrochemical active surface of this catalyst is high, good endurance, and after 4500 enclose, electrochemical active surface still has the holding of 54%.In the chronoamperometry electro-chemical test of 120 minutes, current density decay is less, shows higher electro-chemical activity, higher current density and more superior durability. |