| titleOfInvention | A kind of cross-linking modified soybean albumen adhesive |
| abstract | The invention provides a kind of cross-linking modified soybean albumen adhesive and preparation method thereof.Its preparation technology is：Add defatted soy flour, water, neopelex, alkali in reactor, after stirring 5 minutes, add ethylene glycol, silicone oil, temperature is risen to into 90 DEG C, and insulated and stirred 3 hours, cool down blowing.Adhesive is added two or more in epoxy resin, melamine resin, Lauxite, phenolic resin as crosslinking agent, is well mixed using front.The soybean albumen adhesive preparation process is simple of the present invention, modest viscosity are actual workable.Adhesive has an excellent water resistance, when poplar plywood test specimen is impregnated 1 hour during the water of 2 hours and 63 ± 3 DEG C is boiled in boiling water, the bonding strength >=0.7MPa of sample, and without phenomenon of coming unglued. |