http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-103682296-B
Outgoing Links
| Predicate | Object |
|---|---|
| classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/Y02E60-10 |
| classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B82Y30-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B82Y40-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C01G23-005 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/H01M4-485 |
| classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01M4-485 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C01G23-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B82Y40-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B82Y30-00 |
| filingDate | 2013-08-16-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| grantDate | 2015-12-09-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationDate | 2015-12-09-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationNumber | CN-103682296-B |
| titleOfInvention | A kind of preparation method of nanoscale lithium titanate material with high specific capacity |
| abstract | The invention discloses a kind of preparation method of nanoscale lithium titanate material with high specific capacity, the preparation of it comprises the steps: (1) A liquid: the preparation of (2) B liquid: under the condition of (3) magnetic agitation, B liquid is slowly added in A liquid, obtains mixed dispersion liquid; (4) mixed dispersion liquid is loaded in pyroreaction still, be then placed in baking oven and react, after reaction terminates, naturally cool to room temperature, suction filtration, then with after deionized water or absolute ethanol washing, under the temperature conditions of 60 ~ 120 DEG C, carry out drying, obtain presoma; (5) by presoma, under the temperature conditions of nitrogen atmosphere and 400 ~ 1000 DEG C, sintering 1 ~ 5h; Obtain nanoscale lithium titanate material; (6) by nanoscale lithium titanate material, be in the acid solution of 0.01mol/L ~ 14mol/L in hydrionic concentration, under the temperature conditions of 20 ~ 200 DEG C, soak 2 ~ 24h, then suction filtration is carried out, after washing with deionized water or absolute ethyl alcohol again, dry, obtain nanoscale lithium titanate material with high specific capacity. |
| priorityDate | 2013-08-16-04:00^^<http://www.w3.org/2001/XMLSchema#date> |