http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-103464211-B
Outgoing Links
| Predicate | Object |
|---|---|
| classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/Y02E60-50 |
| classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01M4-90 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B01J31-32 |
| filingDate | 2013-09-13-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| grantDate | 2016-09-28-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationDate | 2016-09-28-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationNumber | CN-103464211-B |
| titleOfInvention | A kind of MnOxthe preparation method of/C-PTFE catalyst mastic |
| abstract | A kind of MnO x The preparation method of/C PTFE catalyst mastic, including the configuration of catalyst precursor solution, the preparation of carbon carrier dispersion liquid and MnO x The preparation of/C PTFE catalyst mastic.Compared to the preparation method of conventional metals air battery cathode catalyst mastic, the present invention has and can prepare at normal temperatures and pressures, it is not necessary to the auxiliary equipments such as reactor, saves the preparation cost of catalyst, it is easy to batch production；The steps such as preparation process is simple, eliminates the washing in traditional catalyst preparation process, filters, drying；A step can realize the preparation of catalyst mastic, it is not necessary to first prepare MnO x / C catalyst, then catalyst and PTFE mix and blend are prepared catalyst mastic, preparation flow is simple, it is easy to industrialization；The metal air battery cathodes using catalyst mastic of the present invention to prepare has a higher oxygen reduction activity, and the advantage such as cathode performance concordance is good. |