http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-103401017-B
Outgoing Links
| Predicate | Object |
|---|---|
| classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/Y02E60-10 |
| classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/H01M10-0562 |
| filingDate | 2013-08-02-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| grantDate | 2015-09-23-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationDate | 2015-09-23-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationNumber | CN-103401017-B |
| titleOfInvention | A kind of Li2S-P2S5-TiS2 series non-crystalline state electrolyte |
| abstract | The present invention relates to a kind of Lin 2 s-Pn 2 sn 5 -TiSn 2 series non-crystalline state electrolyte, described electrolyte has high conductivity at room temperature, belongs to lithium ion battery associated materials preparation field.Described electrolyte is prepared by high-energy ball milling reaction and low-temperature solid phase reaction, is specially in the glove box with argon gas atmosphere protection, by three kinds of reaction raw material Lin 2 s, Pn 2 sn 5 , TiSn 2 mix according to the ratio of molar percentage 34:15:1, add agate ball and put into ball grinder, argon gas atmosphere lower seal carries out high-energy ball milling reaction; Then the sample that ball milling is good is placed in tube furnace, at argon gas atmosphere 300 DEG C, fires 3 hours, obtain described amorphous state electrolyte.Described electrolyte, by being combined with low-temperature solid phase reaction by high-energy ball-milling process, has higher conductivity at room temperature, and preparation technology's flow process is simple, and reaction condition is gentle. |