http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-103028864-B
Outgoing Links
Predicate | Object |
---|---|
assignee | http://rdf.ncbi.nlm.nih.gov/pubchem/patentassignee/MD5_72bc97b2e4fbcd1789ea88b40356c638 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B23K35-30 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B23K35-368 |
filingDate | 2012-12-14-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
grantDate | 2014-11-19-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
inventor | http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_01dad16603518d590ed2ffbd8d9ae8fe http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_801f67df7c928553b34c9be02c077562 http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_9cb083a213f752c540d3cf6c2fc6ef77 |
publicationDate | 2014-11-19-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CN-103028864-B |
titleOfInvention | High-strength and high-toughness metal powder type flux-cored wire with no need of being pre-heated before welded |
abstract | The invention provides a high-strength and high-toughness metal powder type flux-cored wire with no need of being pre-heated before welded. Steel skin is 79-84% of a total weight of a welding wire and a flux core is 16-21% of the total weight of the welding wire. The steel skin is manufactured by using a cold rolling carbon steel strip and comprises the following components: 0.02-0.055% of C, 0.005-0.0085% of Si, 0.15-0.35% of Mn and the balance of iron; and the flux core comprises the following components: 12-18% of nickel powder, 2-4% of manganese powder, 3-7% of silicon iron, 2-6% of ferro-molybdenum, 0.8-2.5% of ferrotitanium, 1-5% of mid-carbon ferromanganese, 0.8-2.5% of potassium fluosilicate and rear earth oxide in sum, and the balance of iron powder. The flux-cored wire provided by the invention has the advantages of good welding process, high melting efficiency and less slag quantity; the yield strength of deposited metal can be more than 590 MPa; the impact rigidity at a temperature of -50 DEG C can be more than 70J; and the diffusible hydrogen is in an ultralow hydrogen level. |