| titleOfInvention | Industry wear resistant corrosion resistant crystallizing glass sheet material and preparation method |
| abstract | The present invention relates to a kind of industrial wear resistant corrosion resistant crystallizing glass sheet material and preparation method.The present invention includes the weight ratio ingredient of following raw materials according: chromium slag 10 ~ 30 parts, 15 ~ 30 parts, flyash, gold mine tailings 10 ~ 20 parts, albite 5 ~ 10 parts, quartz sand 10 ~ 30 parts, borax 2 ~ 5 parts calculates material side, ball milling mixing, respectively through founding, shaping, anneal, coring and crystallization obtain crystallizing glass sheet material.The present invention effectively make use of chromium slag, flyash and gold mine tailings, and preparation technology is simple, and production cost is low, the favorable reproducibility of different batches product, is applicable to large-scale industrial production.Obtained slag nucleated glass plate has closely knit, high strength, the excellent performance such as corrosion-resistant, wear-resisting.The inner lining material being applied to power industry, chemical industry, coal industry and the steel industry position such as perishable easy to wear can be widely used in. |