abstract |
A sheet of a 6000 type aluminum alloy containing Si and Mg as main alloy components and having excellent formability sufficient to allow flat hemming, excellent resistance to denting, and good hardenability during baking a coating, which exhibits an anisotropy of Lankford values of more than 0.4 or the strength ratio for cube orientations of the texture thereof of 20 or more, and exhibits a minimum bend radius of 0.5 mm or less at 180° bending even when the offset yield strength thereof exceeds 140 MPa through natural aging; and a method for producing the sheet of the aluminum alloy, which comprises subjecting an ingot to a homogenization treatment, cooling to a temperature lower than 350 C at a cooling rate of 100°C/hr or more, optionally to room temperature, heating again to a temperature of 300 to 500°C and subjecting it to hot rolling, cold rolling the hot rolled product, and subjecting the cold rolled sheet to a solution treatment at a temperature of 500°C or higher, followed by quenching. |