http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CA-2105580-A1
Outgoing Links
Predicate | Object |
---|---|
assignee | http://rdf.ncbi.nlm.nih.gov/pubchem/patentassignee/MD5_1e70c0aeade92d7571d955d3b90ea06e |
classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08L23-08 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08L33-24 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C08L27-06 |
classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08L33-24 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08L33-04 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08L- http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08L23-08 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08L33-00 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08L27-06 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C08J3-00 |
filingDate | 1992-03-06-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
inventor | http://rdf.ncbi.nlm.nih.gov/pubchem/patentinventor/MD5_55935607e408c492d91564d65e09f794 |
publicationDate | 1992-09-07-04:00^^<http://www.w3.org/2001/XMLSchema#date> |
publicationNumber | CA-2105580-A1 |
titleOfInvention | Process for making polyvinyl chloride compositions having high heat distortion temperatures |
abstract | Heat distortion temperature of polyvinyl chloride compositions can be significantly increased above the heat distortion temperature of uncompounded polyvinyl chloride by preblending an imidized acrylic resin having a glass transition temperature above 140 ·C with a third polymer melt-processable throughout the temperature range of 150-300 ·C under conditions where a two-phase blend is formed, wherein the third polymer forms the continuous phase and the imidized acrylic resin forms the dispersed phase and then melt-blending the two-phase blend with polyvinyl chloride at a temperature of 150-220 ·C to form a composition in which the imidized acrylic resin forms a substantially homogeneous blend with polyvinyl chloride. It also is possible to preblend imidized acrylic resin with a third polymer with which it is compatible, for example, another imidized acrylic resin having a sufficiently low glass transition temperature to lower the resulting glass transition temperature of the preblend below about 130 ·C, which then is blended with polyvinyl chloride. |